Preparation of MoS2/Bamboo Photothermal Conversion Material and Its Application in Seawater Desalination
-
摘要: 研究基于缓解淡水资源短缺的目的,采用钼酸钠和硫脲为原料在竹材上水热合成二硫化钼的方法制备2D二硫化钼/竹材光热转换材料,通过海水蒸发测试的实验检验其淡化性能,测试结果显示:在一个太阳光照强度下,蒸发1 h后二硫化钼/竹材的蒸发速率达到1.095 kg·m-2·h-1;光热转换效率达到78.20%;用UV/Vis/NIR测得二硫化钼/竹材在250-2 500 nm波长范围内的最大光吸收率超过80%。表明了二硫化钼/竹材光热转换材料具有较好的光热转换效率。因此,在实验中二硫化钼/竹材表现出良好的光热水蒸发性能,为实现具有绿色和可持续发展的光热蒸发器件的高效利用提供了借鉴和应用基础。Abstract: In order to alleviate the shortage of freshwater resources,a 2-dimensional MoS2/bamboo photothermal conversion material was prepared by hydrothermal synthesis of molybdenum disulfide on bamboo with sodium molybdate and thiourea as raw materials. Its desalination property was examined through the seawater evaporation test. The results showed that the evaporation rate of seawater with MoS2/bamboo reached 1.095 kg m-2·h-1 after one-hour evaporation under one-sun intensity illumination. The light-heat conversion efficiency was 78.20%. And the maximum optical absorptivity of MoS2/bamboo at wavelengths between 250 nm and 2 500 nm measured by UV/Vis/NIR diffuse reflectance spectroscopy exceeded 80%. These indicated that MoS2/bamboo material boasted good photothermal conversion efficiency. Therefore,MoS2/bamboo material in this study had superior photothermal water evaporation performance,which provided reference and application basis for realizing the efficient utilization of green and sustainable photothermal evaporation devices.
-
Key words:
- Solar energy /
- Molybdenum disulfide /
- Bamboo /
- Photothermal conversion /
- Seawater desalination
-
[1] 纪雪. 2025年将有35亿人面临缺水[J].生态经济,2019,35(10):5-8. [2] Elimelech M,Phillip W A. The future of seawater desalination:energy,technology,and the environment[J]. Science,2011,333(6043):712-717. [3] Eliasson J. The rising pressure of global water shortages[J]. Nature,2015,517(7532):6. [4] Oki T,Kanae S. Global hydrological cycles and world water resources[J]. Science,2006,313(5790):1068-1072. [5] Khawaji A D,Kutubkhanah I K,Wie J-M. Advances in seawater desalination technologies[J]. Desalination,2008,221(1-3):47-69. [6] Yin J,Deng B. Polymer-matrix nanocomposite membranes for water treatment[J]. Journal of Membrane Science,2015,479:256-275. [7] Neumann O,Urban A S,Day J,et al. Solar vapor generation enabled by nanoparticles[J]. ACS Nano,2013,7(1):42-49. [8] Zhang P,Li J,Lv L,et al. Vertically aligned graphene sheets membrane for highly efficient solar thermal generation of clean water[J]. ACS Nano,2017,11(5):5087-5093. [9] Wang X,Ou G,Wang N,et al. Graphene-based recyclable photo-absorbers for high-efficiency seawater desalination[J]. ACS Applied Materials&Interfaces,2016,8(14):9194-9199. [10] Zhu R,Liu M,Hou Y,et al. Mussel-inspired photothermal synergetic system for clean water production using full-spectrum solar energy[J]. Chemical Engineering Journal,2021,423:129099. [11] Liu J,Yao J,Yuan Y,et al. Surface-carbonized bamboos with multilevel functional biostructures deliver high photothermal water evaporation performance[J]. Advanced Sustainable Systems,2020,4(9):2000126. [12] Feng Q,Bu X,Wan Z,et al. An efficient torrefaction bamboo-based evaporator in interfacial solar steam generation[J]. Solar Energy,2021,230:1095-1105. [13] Zhang G,Zhang Y-W. Thermal properties of two-dimensional materials[J]. Chinese Physics B,2017,26(3):034401. [14] Guo Z,Wang G,Ming X,et al. PEGylated self-growth MoS2 on cotton cloth substrate for high-efficiency solar energy utilization[J]. ACS Applied Materials&Interfaces,2018,10(29):24583-24589. [15] Darus S A A Z M,Ghazali M J,Azhari C H,et al. Physicochemical and thermal properties of lignocellulosic fiber from Gigantochloa scortechinii bamboo:effect of steam explosion treatment[J]. Fibers and Polymers,2020,21(10):2186-2194. [16] Guo F,Zhang X,Yang R,et al. Hygroscopicity,degradation and thermal stability of isolated bamboo fibers and parenchyma cells upon moderate heat treatment[J]. Cellulose,2021,28(13):8867-8876. [17] Ding S,He P,Feng W,et al. Novel molybdenum disulfide nanosheets-decorated polyaniline:preparation,characterization and enhanced electrocatalytic activity for hydrogen evolution reaction[J]. Journal of Physics and Chemistry of Solids,2016,91:41-47. [18] Pisal K B,Thorat A S,Jagtap S S,et al. Synthesis and characterization of hydrothermally prepared molybdenum disulfide for supercapacitor application[J]. Materials Today:Proceedings,2021,43(4):2707-2710. [19] 范必涛.竹质基纤维素纳米纤维功能化气凝胶的研究[D].杭州:浙江农林大学,2017. [20] Chen C,Kuang Y,Hu L. Challenges and opportunities for solar evaporation[J]. Joule,2019,3(3):683-718.
点击查看大图
计量
- 文章访问数: 419
- HTML全文浏览量: 60
- PDF下载量: 137
- 被引次数: 0